Vinyl Chloride Copolymer Emulsion (Promotion)
Share to:

Vinyl Chloride Copolymer Emulsion (Promotion)

Vinyl Chloride Copolymer Emulsion

         Products

 Test Items

VCAR-80

VCAR-70S

VCAR-60

VDAR-20S

VDAR-4

VDAR-(-21)

Solid content%

48±2

48±2

48±2

48±2

48±2

47±2

Viscosity,s(25℃,T-4# cup)

11-20

11-20

10-18

10-18

10-18

11-20

 Glass Transition Temp 

80

68

58

30

4

-15

Minimum Film Forming Temp 

81-83

64-66

60-62

28-30

6-8

<0

pH

7-8

7-8

7-8

2-5

2-4

4-5

Particle Size,μm

0.2-0.3

0.2-0.3

0.2-0.3

0.2-0.3

0.2-0.3

0.1-0.2

Calcium ion stability

0.5%CaCl2 solution)

OK

mechanical stability

2000rpm)

OK

Storage stability

50℃,30D)

OK

Applications

Grade

Performance

Applications

VCAR-80

Good adhesion to PVC and wood, high hardness, good abrasion resistance

Plastic paint, Wood Sealing Primer and PVC ink.

VCAR-70S

Good adhesion to PVC, fast drying speed, good water resistance

Applicate in printing ink, paper processing & surface treatment of leather

VCAR-60

Good adhesion to plastic substrate, good compatibility with pigment, fast drying speed, good alcohol resistance, and good water resistance

Applicate in primer of plastic substrate for PVC, ABS,& PC

VDAR-20S

Good compatibility with pigment, antirust, without heavy metal. Good water resistance, alcohol resistance and saltwater resistance

Applicate in anti-corrosive primer in heavy metal, it can replace alkyd lacquer

VDAR-4

Good film forming, high oxygen index 

It can replace brominated flame retardant

VDAR-(-21)

Good mechanical stability, good weather resistance, good abrasive resistance, good adhesion to cellulose ,the amount of glue is small used in the surface treatment, and the carbon layer after combustion is kept intact.

Applicate in Back coating, flocking adhesive, carpet back coating and back coating of industrial textiles, it is similar to the Lubrizols PVC series emulsion.